- LG Chemical LUPOS HR-2207 Heat Resistant SAN, 20% Glass Fiber Reinforced
LG Chemical LUPOS HR-2207 Heat Resistant SAN, 20% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUPOS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOS HR-2207 Heat Resistant SAN, 20% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have a wide range of applications in automotive parts, electrical/electronic parts. and industrial equipments, etc.Applications: Automotive: Main core, glove box, meter box, head lamp housing, back mirror cover, etc.Electrical and Electronic: Computer tape reel, pan cake hub for video and audio, stereo speaker box, fan for air conditioner, washing machine pulley, fax frameOthers:Camera body, fishing reel, bobbinInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 118 MPa | 17100 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 7.35 GPa | 1070 ksi | ASTM D790 |
| Izod Impact, Notched | 0.390 J/cm @Temperature 23.0 °C |
0.731 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 90.0 °C | 194 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 78.45 - 88.26 MPa | 11380 - 12800 psi | Second |
| 68.65 - 98.07 MPa | 9957 - 14220 psi | First | |
| Back Pressure | 0.000 - 3.92 MPa | 0.000 - 569 psi | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C4220 PC+ABS
- SABIC Innovative Plastics Lexan® 101R PC (Asia Pacific)
- TSE Industries EcoWIND® 100 Polyurethane Resin Filament Winding (discontinued **)
- LyondellBasell Lupolen® 3020 H LDPE, Film Grade
- Ineos R35C-02 Polypropylene Random Copolymer
- GRECO ISOPAK 569 ABS Resin
- Kraton® D1191 E (SBS) Radial Block Copolymer
- Lucite International Diakon® TD525 Toughened Acrylic Compound
- Asahi Kasei Thermofil P-20TC-1628 20% Talc Filled, Heat Stabilized
- Aremco Corr-Paint™ CP3015-GR High Temperature Protective Coating Inorganic, Mixed Oxides Filled
Copyright © lookpolymers.com All Rights Reserved