- LG Chemical LUCEL FW700N Modified POM, Friction Resistance, Abrasion Resistance
LG Chemical LUCEL FW700N Modified POM, Friction Resistance, Abrasion Resistance
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUCEL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCEL FW700N Modified POM, Friction Resistance, Abrasion Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, Modified POM, Friction Resistance, Abrasion ResistanceApplication: Gears, Printer Roller Pumps, Gear Worm WheelsCAS No. 66455-31-0Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.10 | 0.10 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.018 - 0.022 cm/cm @Thickness 3.20 mm |
0.018 - 0.022 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C |
15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.7 MPa @Thickness 3.20 mm |
7790 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 34 % @Thickness 3.20 mm |
34 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 70.3 MPa @Thickness 3.20 mm |
10200 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 1.8061 GPa @Thickness 3.20 mm |
261.95 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.451 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
0.845 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| Front Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Nozzle Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 90.0 - 110 °C | 194 - 230 °F | Injection Molding |
| Dry Time | 2.00 - 3.00 hour | 2.00 - 3.00 hour | Injection Molding |
| Back Pressure | 0.490 - 3.04 MPa | 71.1 - 441 psi | Injection Molding |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 131 PC (Asia Pacific)
- PolyOne Edgetek® QT-20MN/000 natural HI Syndiotactic Polystyrene (SPS)
- Ineos Nova 3504 General Purpose Crystal Polystyrene (discontinued **)
- ExxonMobil Escorene® LD-411 LDPE Power Cable Insulation (discontinued **)
- Metton LMR M2100VO Liquid Molding Resin
- Techmer ES HiFill® PA6 GF50 IM L NAT001 50% Glass Filled
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR Sulfur
- Eurotec® Tecopet® PT70 KK45 PET, 45% glass fiber/mineral reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- Adamas Adalon® 814 PTFE, 55% Bronze, 5% MoS2
- BASF 3-Amino-1-propanol
Copyright © lookpolymers.com All Rights Reserved