LG Chemical KEYFLEX BT 3038D Ester Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX BT 3038D Ester Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPC-ET, Functional, Fast Molding, Low ModulusApplication: Automotive Interior, Soft Touch GripsCAS: 37282-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Molecular Weight | 458.458 g/mol | 458.458 g/mol | |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| 0.010 | 0.010 | Extrusion Molding | |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Hardness, Shore D | 35 | 35 | ASTM D2240 |
| Tensile Strength at Break | 22.6 MPa @Thickness 2.00 mm |
3280 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 700 % @Thickness 2.00 mm |
700 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Izod Impact, Notched | NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature -40.0 °C |
NB @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 190 °C | 374 °F | Peak |
| Boiling Point | 140 - 230 °C | 284 - 446 °F | |
| Flash Point | 300 - 340 °C | 572 - 644 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 205 - 235 °C | 401 - 455 °F | Injection Molding |
| Middle Barrel Temperature | 205 - 225 °C | 401 - 437 °F | Injection Molding |
| Front Barrel Temperature | 215 - 235 °C | 419 - 455 °F | Injection Molding |
| Nozzle Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Zone 1 | 205 - 220 °C | 401 - 428 °F | Extrusion Molding |
| Zone 2 | 210 - 230 °C | 410 - 446 °F | Extrusion Molding |
| Zone 3 | 215 - 235 °C | 419 - 455 °F | Extrusion Molding |
| Zone 4 | 215 - 235 °C | 419 - 455 °F | Extrusion Molding |
| Adapter Temperature | 215 - 235 °C | 419 - 455 °F | Extrusion Molding |
| Die Temperature | 205 - 245 °C | 401 - 473 °F | Extrusion Molding |
| Melt Temperature | 205 - 235 °C | 401 - 455 °F | Injection Molding |
| 205 - 235 °C | 401 - 455 °F | Extrusion Molding | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | Injection Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| 80.0 - 90.0 °C | 176 - 194 °F | Extrusion Molding | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 121SRM PC (Asia Pacific)
- Victrex® ST™ ST45CA30 PolyEtherKetoneEtherKetoneKetone, 30% Carbon Fibre Reinforced
- LyondellBasell Montell HB312CM UHMW Polyethylene
- MetalTek MTEK CX-2MW Cast UNS N26022 Severe Corrosion and Heat Resistant Alloy
- Styrolution PS 3100/3101 GPPS
- Chevron Phillips K-Resin® BK10 Styrene-Butadiene Copolymer, Injection Molding Grade
- ExxonMobil Exxtral™ CNK 010 Performance Polyolefin
- EMS-Grivory Grivory® TR XE 4010 PA*-I
- Axiall 6300 Rigid PVC, Molding
Copyright © lookpolymers.com All Rights Reserved