DSM Arnite® TZ6 280 PBT-(GF+GB)40

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled
Manufacturer DSM Engineering Plastics
Trade Name Arnite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Arnite® TZ6 280 PBT-(GF+GB)40.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Reinforced, 20% Glass Beads Reinforced
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ISO 1183
Water Absorption 0.25 %
0.25 %
Sim. To ISO 62
Moisture Absorption 0.150 %
0.150 %
Sim. To ISO 62
Viscosity 20000 cP

@Shear Rate 100000 1/s,
Temperature 230 °C
 20000 cP

@Shear Rate 100000 1/s,
Temperature 446 °F
20000 cP

@Shear Rate 100000 1/s,
Temperature 250 °C
 20000 cP

@Shear Rate 100000 1/s,
Temperature 482 °F
20000 cP

@Shear Rate 100000 1/s,
Temperature 270 °C
 20000 cP

@Shear Rate 100000 1/s,
Temperature 518 °F
300000 cP

@Shear Rate 1.00 1/s,
Temperature 270 °C
 300000 cP

@Shear Rate 1.00 1/s,
Temperature 518 °F
500000 cP

@Shear Rate 1.00 1/s,
Temperature 250 °C
 500000 cP

@Shear Rate 1.00 1/s,
Temperature 482 °F
700000 cP

@Shear Rate 1.00 1/s,
Temperature 230 °C
 700000 cP

@Shear Rate 1.00 1/s,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 100 MPa
14500 psi
ISO 527-1/-2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 8.70 GPa
1260 ksi
ISO 527-1/-2
Charpy Impact Unnotched 4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²

@Temperature 23.0 °C
 2.62 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 75.0 µm/m-°C
41.7 µin/in-°F
ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093