LG Chemical KEYFLEX BT 1047D Ester Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX BT 1047D Ester Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPC-ET, General Purpose, Medium ModulusApplication: Antenna Cover, Injection Parts for Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Molecular Weight | 458.458 g/mol | 458.458 g/mol | |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| 0.010 | 0.010 | Extrusion Molding | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.012 cm/cm @Thickness 3.20 mm |
0.0080 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 23 g/10 min @Load 2.16 kg, Temperature 220 °C |
23 g/10 min @Load 4.76 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength at Break | 29.4 MPa @Thickness 2.00 mm |
4260 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 600 % @Thickness 2.00 mm |
600 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Flexural Modulus | 0.0981 GPa @Thickness 6.40 mm |
14.2 ksi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature -40.0 °C |
NB @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 | |
| Tear Strength | 127 kN/m | 728 pli | 50mm/min, at Break; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 190 °C | 374 °F | Peak |
| Boiling Point | 140 - 230 °C | 284 - 446 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C @Thickness 6.40 mm |
158 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Flash Point | 300 - 340 °C | 572 - 644 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 26.0 kV/mm @Thickness 1.00 mm |
660 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Zone 1 | 190 - 230 °C | 374 - 446 °F | Extrusion Molding |
| Zone 2 | 190 - 210 °C | 374 - 410 °F | Extrusion Molding |
| Zone 3 | 200 - 220 °C | 392 - 428 °F | Extrusion Molding |
| Zone 4 | 210 - 230 °C | 410 - 446 °F | Extrusion Molding |
| Adapter Temperature | 210 - 230 °C | 410 - 446 °F | Extrusion Molding |
| Die Temperature | 200 - 240 °C | 392 - 464 °F | Extrusion Molding |
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Injection Molding |
| 190 - 230 °C | 374 - 446 °F | Extrusion Molding | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | Injection Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| 80.0 - 90.0 °C | 176 - 194 °F | Extrusion Molding | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- Polymer Resources PC-HM-FR1 Polycarbonate, 10% Glass Reinforced, Flame Retardant
- Kraton® G1654 H (SEBS) Linear Triblock Copolymer
- SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+PS
- Samsung Cheil Industries Starex® TF-0959 T HI-PMMA
- Solvay JAGUAR® EXCEL Surfactant
- Taiwan Sheen Soon Sheenthane® AH-571 TPU for Hotmelt Adhesive
- Tipco Tipcolene® UV 1006 - Combination of UV Stabilizer & UV Absorber Masterbatch with 15% UV & Anti-Oxidants in LDPE
- Bulk Molding Compounds BMC 400 Thermoset Polyester, Low Shrink, High Strength, Electrical Grade
Copyright © lookpolymers.com All Rights Reserved