LG Chemical KEYFLEX BT 10288D Ester Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX BT 10288D Ester Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPC-ET, General Purpose, Low ModulusApplication: Automotive Interior, Soft Touch GripsCAS: 37282-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.80 % @Temperature 23.0 °C, Time 86400 sec |
0.80 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Molecular Weight | 458.458 g/mol | 458.458 g/mol | |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| 0.010 | 0.010 | Extrusion Molding | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 230 °C |
25 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | ASTM D2240 |
| Hardness, Shore D | 25 | 25 | ASTM D2240 |
| Tensile Strength at Break | 19.6 MPa @Thickness 2.00 mm |
2840 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 900 % @Thickness 2.00 mm |
900 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Izod Impact, Notched | NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature -40.0 °C |
NB @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 155 °C | 311 °F | Peak |
| Boiling Point | 140 - 230 °C | 284 - 446 °F | |
| UL RTI, Electrical | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| 50.0 °C @Thickness >=3.00 mm |
122 °F @Thickness >=0.118 in |
||
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| 50.0 °C @Thickness >=3.00 mm |
122 °F @Thickness >=0.118 in |
||
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness >=1.50 mm |
122 °F @Thickness >=0.0591 in |
|
| 50.0 °C @Thickness >=3.00 mm |
122 °F @Thickness >=0.118 in |
||
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
|
| HB @Thickness >=3.00 mm |
HB @Thickness >=0.118 in |
||
| Flash Point | 300 - 340 °C | 572 - 644 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| Middle Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Front Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Nozzle Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Zone 1 | 160 - 180 °C | 320 - 356 °F | Extrusion Molding |
| Zone 2 | 170 - 190 °C | 338 - 374 °F | Extrusion Molding |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | Extrusion Molding |
| Zone 4 | 180 - 200 °C | 356 - 392 °F | Extrusion Molding |
| Adapter Temperature | 180 - 200 °C | 356 - 392 °F | Extrusion Molding |
| Die Temperature | 170 - 210 °C | 338 - 410 °F | Extrusion Molding |
| Melt Temperature | 160 - 200 °C | 320 - 392 °F | Injection Molding |
| 160 - 200 °C | 320 - 392 °F | Extrusion Molding | |
| Mold Temperature | 10.0 - 35.0 °C | 50.0 - 95.0 °F | Injection Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| 80.0 - 90.0 °C | 176 - 194 °F | Extrusion Molding | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- Radici Radilon® S 40FL (cond.) Nylon 6
- Lotte Chemical Titan TITANEX® LF1051 Linear low density polyethylene Hexene-1 resin (discontinued **)
- PolyOne Lubri-Tech™ NL-40GB/15T Nylon 6/12 - 40% Glass Bead Reinforced - 15% PTFE Lubricated (discontinued **
- Karina 700-48/1-B-IS-BZ. Black PVC Compound
- Less Common Metals Lanthanum Vacuum Remelted Rare Earth Metal
- Karina 760-48/1-E-AC-LF Black PVC Compound
- Samyang Triel® 5450 Thermoplastics Polyetherester Elastomer, General Extrusion
- BASF Neopolen® P 8225 K 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- Arlon 51149R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Techmer ES HiFill FR® PA6 GF20 FR HS L 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved