- DuPont Elvax® 40L-03 Low Smoke Non-halogen Jacket Formulation (discontinued **)
DuPont Elvax® 40L-03 Low Smoke Non-halogen Jacket Formulation (discontinued **)
| Category | Polymer , Thermoplastic , Ethylene Vinyl Acetate |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvax® 40L-03 Low Smoke Non-halogen Jacket Formulation
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvax® 40L-03 low smoke non-halogen jackets.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 39 @Temperature 100 °C |
39 @Temperature 212 °F |
ML 1 + 4; ASTM D1646 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 12.0 MPa | 1740 psi | Extruded wire; ASTM D412 |
| 13.2 MPa | 1910 psi | After 7 days/150°C air oven, ASTM D573 | |
| 10.32 MPa @Treatment Temp. 121 °C, Time 64800 sec |
1497 psi @Treatment Temp. 250 °F, Time 18.0 hour |
in ASTM #2 Oil | |
| Elongation at Break | 173.8 % | 173.8 % | After 7 days/150°C air oven; ASTM D573 |
| 220 % | 220 % | Extruded wire; ASTM D412 | |
| 149.6 % @Treatment Temp. 121 °C, Time 64800 sec |
149.6 % @Treatment Temp. 250 °F, Time 18.0 hour |
in ASTM #2 Oil | |
| Tear Strength | 7.00 kN/m | 39.9 pli | ASTM D470 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -35.0 °C | -31.0 °F | ASTM D746 |
| NBS Smoke Density | <= 23 | <= 23 | Flaming mode; ASTM E662 |
| <= 146 | <= 146 | Non-flaming mode; ASTM E662 | |
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| a,a'-bis [t-butylperoxy] diisopropylbenzene | 2.5 phr | |
| Antioxidant | 1.5 phr | |
| Elvax® 40L-03 | 100 phr | |
| HVA-2 | 1 phr | |
| Hydrated Alumina | 150 phr | |
| Silquest A-172 | .75 phr | |
| SRF Carbon Black | 5 phr | |
| Stearic Acid | 1 phr | |
| Volume Swell | 0.58 | After 18hr/121°C in ASTM #2 Oil |
| 0.9 | After 70hr/100°C in ASTM #3 Oil |
Users viewing this material also viewed the following:
- Permabond LM113 Anaerobic Threadlocker
- ExxonMobil Santoprene® 912BA Thermoplastic Elastomer (discontinued **)
- Lehmann & Voss LUVOCOM® 80-7884 Polyacetal-copolymer, with carbon fiber
- Huntsman AVALON® 65 AE Thermoplastic Polyurethane
- A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66
- Fainplast Compounds CL 76 Flexible PVC, Sheathing
- Hippe EP GC 41 Woven Glass Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod
- Carpenter Pyromet® CTX-3 Superalloy, Heat Treatment for Brazing Cycles over 982°C
- ATI Allegheny Ludlum 425 Mod Martensitic Stainless Steel
- Pasargad Polymer Peyvand Pasamid 3P-M2000W Nylon 66
Copyright © lookpolymers.com All Rights Reserved