- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- LG Chemical HI110 ABS, High Impact, Chemical Resistance
LG Chemical HI110 ABS, High Impact, Chemical Resistance
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical HI110 ABS, High Impact, Chemical Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, High Impact, Chemical ResistanceApplication: Edge of Furniture ApplicationsCAS No. 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Melt Flow | 11 g/10 min @Load 10.0 kg, Temperature 220 °C |
11 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 87 | 87 | ASTM D785 |
| Tensile Strength, Yield | 37.3 MPa @Thickness 3.20 mm |
5400 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | >= 10 % @Thickness 3.20 mm |
>= 10 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 3.20 mm |
270 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 4.02 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
7.53 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Nozzle Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- LG Chemical LUPOS GP2305A SAN+GF30%, General Purpose
- H.C. Starck Amperit® 740.8 Aluminum Oxide (Al2O3)
- Heatbath/Park Pack Carburizer BF#21
- Techmer ES HiFill FR® PC IM FR
- SABIC Innovative Plastics LNP THERMOCOMP UF003AS PPA (Europe-Africa-Middle East)
- Unitika E-RUNG60 PA66, 60% Glass Fiber Reinforced, Dry
- DuPont Teijin Films Teijin® Tetoron® HSL Polyester Film, 700 Gauge
- COI Ceramics Sylramic™ Crystalline Silicon Carbide (SiC) Fiber
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N220 (ISAF) Filler
- Ineos H03W-00 Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved