- Asahi Kasei Xyron® SZ800 Modified Polyphenylene Ether
Asahi Kasei Xyron® SZ800 Modified Polyphenylene Ether
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® SZ800 Modified Polyphenylene Ether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-Heat ResistantInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 70 % | 70 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 107 MPa | 15500 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
3.30 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 65.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
36.1 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | 50% RH; ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | 50% RH; ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1e+6 Hz |
2.8 @Frequency 1e+6 Hz |
50% RH; ASTM D150 |
| 2.8 @Frequency 1e+6 Hz |
2.8 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Dielectric Strength | 30.0 kV/mm @Thickness 2.00 mm |
762 kV/in @Thickness 0.0787 in |
Short time; ASTM D149 |
| Dissipation Factor | 0.0027 @Frequency 60 Hz |
0.0027 @Frequency 60 Hz |
50% RH; ASTM D150 |
| 0.0027 @Frequency 1e+6 Hz |
0.0027 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Arc Resistance | 80 sec | 80 sec | Tungsten; ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 - 320 °C | 536 - 608 °F | Resin Temperature |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 90.0 - 120 °C | 194 - 248 °F | Pre-drying Temperature |
| Dry Time | 2 - 4 hour | 2 - 4 hour |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87549 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Abatron AboWeld 8101-9/AboCure 8101-9 Epoxy (discontinued **)
- Taiwan PU Corporation TPUI-H90 High Hydrolysis Resistance, Injection Molding Polyether Base TPU
- Hexcel® HexPly® EH04 Epoxy Resin System, IM4 Fiber
- A. Schulman INVISION™ FX-9090UE Soft Touch Polyolefin Thermoplastic
- CMW® 3 Copper Alloy
- BASF tert.-Butylamine
- ACC QM 135 QSI Quantum Silicones 35 Durometer Condensation Cured Moldmaking Material
- ChevronTexaco Havoline® SAE 10W-30 Synthetic Blend Motor Oil
Copyright © lookpolymers.com All Rights Reserved