- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- LG Chemical BM662B ABS, Heat Resistance
LG Chemical BM662B ABS, Heat Resistance
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical BM662B ABS, Heat Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Blow Molding, Heat ResistanceApplication: Automotives Exterior Housing (Spoiler, Bumper Guard etc.)CAS No. 25120-20-1, 9003-56-9, 25747-74-7 and 31621-07-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Blow Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
2.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Tensile Strength, Yield | 45.1 MPa @Thickness 3.20 mm |
6540 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 30 % @Thickness 3.20 mm |
30 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 70.6 MPa @Thickness 3.20 mm |
10200 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 2.11 GPa @Thickness 3.20 mm |
306 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
2.39 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 1.27 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.39 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 0.686 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
1.29 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 |
| 0.686 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
1.29 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 106 °C @Load 1.00 kg |
223 °F @Load 2.20 lb |
120°C/h; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 200 °C | 356 - 392 °F | Blow Molding |
| Zone 2 | 190 - 210 °C | 374 - 410 °F | Blow Molding |
| Zone 3 | 190 - 210 °C | 374 - 410 °F | Blow Molding |
| Zone 4 | 200 - 220 °C | 392 - 428 °F | Blow Molding |
| Adapter Temperature | 220 °C | 428 °F | Blow Molding |
| Die Temperature | 220 °C | 428 °F | |
| Melt Temperature | 200 - 210 °C | 392 - 410 °F | Blow Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Blow Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Blow Molding |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 GV40 Nylon 6.6 for injection molding, 40% glass fiber reinforced
- Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled
- Indium Corp. Indalloy 33 Bismuth Solder Alloy
- SABIC Innovative Plastics LNP THERMOCOMP RFZ22S PA 66
- Tisan TISOPLEN® 30% Glass Fiber Reinforced Heat Stabilized Copolymer Polypropylene
- Wieland Porta Maximum NF PFM Alloy
- Zircar Zirconia ZYP-55 Zirconia Powder
- ChevronTexaco Vistac® ISO 46 Rock Drill Oil
- Quantum Composites QC-8704FR 63% Glass Fiber Flame Retardant Vinyl Ester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved