Lubrizol Estane® 58070 Thermoplastic Polyurethane

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTANE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol Estane® 58070 Thermoplastic Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Outstanding resiliency, fuel resistance and low temperature flexibility.Uses: Hose and Tube, Injection Molding, Fabric Coating and Wire/CableAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation Provided by The Lubrizol Corporation

Physical Properties	Metric	English	Comments
Specific Gravity	1.17 g/cc	1.17 g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	72 @Time 5.00 sec	72 @Time 0.00139 hour	ASTM D2240
Tensile Strength	45.0 MPa	6530 psi	ASTM D412
	39.6 MPa @Temperature 25.0 °C, Time 2.42e+6 sec	5740 psi @Temperature 77.0 °F, Time 672 hour	ASTM Fuel B; ASTM D412
	45.0 MPa @Temperature 136 °C, Time 605000 sec	6530 psi @Temperature 277 °F, Time 168 hour	Air Oven; ASTM D412
	45.0 MPa @Temperature 25.0 °C, Time 2.42e+6 sec	6530 psi @Temperature 77.0 °F, Time 672 hour	ASTM Fuel A; ASTM D412
Tensile Strength, Yield	600 MPa	87000 psi	100% elongation; ASTM D412
	900 MPa	131000 psi	300% elongation; ASTM D412
Elongation at Break	700 %	700 %	ASTM D412
	630 % @Temperature 136 °C, Time 605000 sec	630 % @Temperature 277 °F, Time 168 hour	Air Oven; ASTM D412
	700 % @Temperature 25.0 °C, Time 2.42e+6 sec	700 % @Temperature 77.0 °F, Time 672 hour	ASTM Fuel A; ASTM D412
	700 % @Temperature 25.0 °C, Time 2.42e+6 sec	700 % @Temperature 77.0 °F, Time 672 hour	ASTM Fuel B; ASTM D412
Tensile Modulus	0.00260 GPa @Temperature 25.0 °C	0.377 ksi @Temperature 77.0 °F	Gehman Rigidity; ASTM D1053
	0.00310 GPa @Temperature -20.0 °C	0.450 ksi @Temperature -4.00 °F	Gehman Rigidity; ASTM D1053
	0.00370 GPa @Temperature -30.0 °C	0.537 ksi @Temperature -22.0 °F	Gehman Rigidity; ASTM D1053
	0.00700 GPa @Temperature -40.0 °C	1.02 ksi @Temperature -40.0 °F	Gehman Rigidity; ASTM D1053
	0.0917 GPa @Temperature -50.0 °C	13.3 ksi @Temperature -58.0 °F	Gehman Rigidity; ASTM D1053
Tear Strength	17.5 kN/m	100 pli	Trouser; ASTM D470
Graves Tear Strength	78.9 kN/m	450 pli	Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles	50	50	H18; ASTM D3389

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F	DSC
Glass Transition Temp, Tg	-52.0 °C	-61.6 °F	DSC

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	175 °C	347 °F	Injection
Middle Barrel Temperature	180 °C	356 °F	Injection
Front Barrel Temperature	195 °C	383 °F	Injection
Nozzle Temperature	200 °C	392 °F	Injection
Zone 1	165 °C	329 °F	Extrusion
Zone 2	170 °C	338 °F	Extrusion
Zone 3	175 °C	347 °F	Extrusion
Zone 4	180 °C	356 °F	Extrusion
Adapter Temperature	180 °C	356 °F	5, Extrusion
Die Temperature	180 °C	356 °F	6, Zone 1, Extrusion
	180 °C	356 °F	Zone 2, Extrusion
Melt Temperature	200 °C	392 °F	Injection
Drying Temperature	82.0 °C	180 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Dew Point	-40.0 °C	-40.0 °F
Injection Pressure	34.5 - 68.9 MPa	5000 - 10000 psi	Injection
Hold Pressure	13.8 - 55.2 MPa	2000 - 8000 psi	Injection
Back Pressure	0.000 - 6.89 MPa	0.000 - 1000 psi	Injection
Screw Speed	50 - 100 rpm	50 - 100 rpm	Injection