LATI Latiohm 73-09 PD01 G/20 POM, 20% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 20% Glass Fiber Reinforced
Manufacturer	LATI
Trade Name	Latiohm
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiohm 73-09 PD01 G/20 POM, 20% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semiconductive/dissipative product based on Polyoxymethylene (POM). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.55 g/cc	0.0560 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0040 - 0.0065 cm/cm	0.0040 - 0.0065 in/in
Linear Mold Shrinkage, Transverse	0.010 - 0.013 cm/cm	0.010 - 0.013 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	110 MPa	16000 psi
Elongation at Break	1.5 %	1.5 %
Tensile Modulus	12.0 GPa	1740 ksi
Charpy Impact Unnotched	2.00 J/cmÂ²	9.52 ft-lb/inÂ²
Charpy Impact, Notched	0.600 J/cmÂ²	2.86 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	165 Â°C	329 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	160 Â°C	320 Â°F
Vicat Softening Point	155 Â°C @Load 5.00 kg	311 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	4000 ohm-cm	4000 ohm-cm
Surface Resistance	1600 ohm	1600 ohm

Processing Properties	Metric	English
Melt Temperature	180 - 210 Â°C	356 - 410 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	80.0 - 100 Â°C @Time 10800 sec	176 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa