- LATI Latiohm 62-09 PD01 G/20-V2HF PA6, 20% Glass Fiber Reinforced, Flame Retardant
LATI Latiohm 62-09 PD01 G/20-V2HF PA6, 20% Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | LATI |
| Trade Name | Latiohm |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latiohm 62-09 PD01 G/20-V2HF PA6, 20% Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Semiconductive/dissipative product based on Polyamide 6 (PA6). Glass fibers. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free. Very good mechanical properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0055 cm/cm | 0.0030 - 0.0055 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | |
| Elongation at Break | 2.3 % | 2.3 % | |
| Tensile Modulus | 10.5 GPa | 1520 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | |
| Vicat Softening Point | 210 °C @Load 5.00 kg |
410 °F @Load 11.0 lb |
|
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
|
| V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
||
| V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+8 ohm | 1.00e+8 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- MV Labs PD460 K2PdCl6 Potassium hexachloropalladate(IV)
- MV Labs PR500 PrF3 Praseodymium fluoride
- Polimeri Europa Europrene® 1502 Emulsion Styrene-Butadiene Rubber
- Kingfa JH710 G10D Flame Retardant & 10% Glass Fiber Reinforced PC
- LTL Color Compounds ColorRxâ„¢ PP1-2000RX Biocompatible Polypropylene Homopolymer
- Borealis Borecene Compact™ RM8346RC Black Linear Polyethylene for Rotational Molding
- ChevronTexaco 460 Honor Ashless AW
- DuPont™ Elvax® 3128-1 Ethylene Vinyl Acetate
- CMW® ELKONITE® 2050C Copper Tungsten Contact Material ASTM B702, Class A, infiltrated
Copyright © lookpolymers.com All Rights Reserved