- Nilit FRIANYL A63 HH-FK 1020 Nylon 6.6 for injection molding, 10% glass fiber and 20% glass ball reinforced
Nilit FRIANYL A63 HH-FK 1020 Nylon 6.6 for injection molding, 10% glass fiber and 20% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 HH-FK 1020 Nylon 6.6 for injection molding, 10% glass fiber and 20% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.4 % | 1.5 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 7.0 % | 5.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 167 MPa | 24200 psi | ISO 2039-1 |
| Tensile Strength at Break | 118 MPa | 17100 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 6.40 GPa | 928 ksi | ISO 527 |
| Flexural Strength | 111 MPa | 16100 psi | ISO 178 |
| Flexural Modulus | 5.10 GPa | 740 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.40 J/cm² | 16.2 ft-lb/in² | ISO 179/1eU |
| 2.90 J/cm² @Temperature -30.0 °C |
13.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.390 J/cm² | 1.86 ft-lb/in² | ISO 179/1eA |
| 0.350 J/cm² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3675 TPE, PP Overmold or Standalone use
- Solvay Specialty Polymers Amodel® A-1133 DW Polyphthalamide (PPA) (discontinued **)
- PolyMirae Moplen EP540R Injection Molding Grade Polypropylene
- LyondellBasell Petrothene® NA373242 Low Density Polyethylene, Cast/Blown Film Grade
- SABIC Innovative Plastics LNP THERMOCOMP AF004L ABS (Asia Pacific)
- Universal Wire Works 5056 (AMS 4182) Aluminum Alloy Filler Metal
- ChevronTexaco SAE 40 Military Symbol 9250 Engine Oil
- Unifrax Fiberfrax® QF-150™ Coating Cement
- E-Polymers EFLEX® V2080 SEBS/TPV
- ExxonMobil LDPE LD 306.38 Low Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved