LATI Latiohm 62-03 PD01 G/20 PPA, 20% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer	LATI
Trade Name	Latiohm
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiohm 62-03 PD01 G/20 PPA, 20% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semiconductive/dissipative product based on Polyamide 6 (PA6). Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.35 g/cc	0.0488 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0030 - 0.0055 cm/cm	0.0030 - 0.0055 in/in
Linear Mold Shrinkage, Transverse	0.0065 - 0.0095 cm/cm	0.0065 - 0.0095 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	200 MPa	29000 psi
Elongation at Break	2.5 %	2.5 %
Tensile Modulus	15.4 GPa	2230 ksi
Charpy Impact Unnotched	6.50 J/cmÂ²	30.9 ft-lb/inÂ²
Charpy Impact, Notched	0.900 J/cmÂ²	4.28 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	220 Â°C	428 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	210 Â°C	410 Â°F
Vicat Softening Point	215 Â°C @Load 5.00 kg	419 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	1000 ohm-cm	1000 ohm-cm
Surface Resistance	1000 ohm	1000 ohm

Processing Properties	Metric	English
Melt Temperature	240 - 280 Â°C	464 - 536 Â°F
Mold Temperature	80.0 - 100 Â°C	176 - 212 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa