LATI Latilub 30/R-07GRT PC, Graphite/PTFE Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled |
| Manufacturer | LATI |
| Trade Name | Latilub |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latilub 30/R-07GRT PC, Graphite/PTFE Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Self-lubricating product based on Polystyrene (PS). Graphite / PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | |
| Elongation at Break | 30 % | 30 % | |
| Elongation at Yield | 1.0 % | 1.0 % | |
| Tensile Modulus | 2.30 GPa | 334 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | |
| Coefficient of Friction, Dynamic | 0.11 | 0.11 | |
| Coefficient of Friction, Static | 0.18 | 0.18 | |
| K (wear) Factor | 100 x 10-8 mm³/N-M | 49.6 x 10-10 in³-min/ft-lb-hr |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
| Vicat Softening Point | 90.0 °C @Load 5.00 kg |
194 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 70.0 - 80.0 °C @Time 10800 sec |
158 - 176 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion LR840 Polyvinyl Chloride, Rigid (PVC, Rigid)
- RheTech Products HP521-187 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 9779 Medium Grey
- Pyrotek MC-1 Metal Ceramic Thermocouple Protection Tube
- Honeywell ACLAR® 22A (1.50 mil) Copolymer Film (discontinued **)
- Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F)
- ELASTO UK Dryflex® 660300S SEBS Based Material, Semi-Filled Qualities, 30A Hardness, Natural
- DuPont Teijin Films Mylar® RL33 Polyester Packaging Film, 100 Gauge
- CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWUVCP 25% Mineral and 15% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Dry
Copyright © lookpolymers.com All Rights Reserved