DuPont Teijin Films Mylar® HS Polyester Film, 65 Gauge (17 µm)

Category	Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer	DuPont Teijin Films (DTF)
Trade Name	Mylar®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Teijin Films Mylar® HS Polyester Film, 65 Gauge (17 µm).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by DuPont Packaging Polymers.An uncoated, transparent polyester packaging film designed for heat shrink applications. It is currently available in 48, 65, 80, and 150 gauges, and other thicknesses may be made available upon request. Adhesive seamed, heat shrinkable tubing and contour bottom heat shrinkable bags made from unsupported Mylar HS, and heat shrinkable heat sealed tubing and bags made from laminations of Mylar HS and a suitable sealant web, are used for packaging.

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	Average value for Mylar® films.
Moisture Vapor Transmission	0.700 cc-mm/m²-24hr-atm	1.78 cc-mil/100 in²-24hr-atm	ASTM E96 Procedure E
Water Vapor Transmission	40.0 g/m²/day	2.58 g/100 in²/day	ASTM E96 Procedure E
Oxygen Transmission	2.10 cc-mm/m²-24hr-atm	5.33 cc-mil/100 in²-24hr-atm	or 125 cc/m²-24hr-atm for the film. ASTM D3985

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	120 %	120 %	ASTM D882
Film Elongation at Break, TD	110 %	110 %	ASTM D882
Modulus of Elasticity	3.10 GPa	450 ksi	(stiffness), ASTM D882
Film Tensile Strength at Break, MD	214 MPa	31000 psi	ASTM D882
Film Tensile Strength at Break, TD	234 MPa	33900 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F	May be used to contain foods during baking above this temperature.
Shrinkage, MD	0.45 % @Temperature 150 °C, Time 1800 sec	0.45 % @Temperature 302 °F, Time 0.500 hour	Film shrinkage
Shrinkage, TD	50 % @Temperature 150 °C, Time 1800 sec	50 % @Temperature 302 °F, Time 0.500 hour	Film shrinkage

Optical Properties	Metric	English	Comments
Haze	10.5 %	10.5 %	ASTM D1003
Transmission, Visible	90 %	90 %	transparent; thickness not quantified