LATI Latigray 82-04 CX/90 PA 12

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	LATI
Trade Name	Latigray
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latigray 82-04 CX/90 PA 12.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radiopaque compound based on Polyamide 12 (PA12). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English	Comments
Density	4.26 g/cc	0.154 lb/inÂ³
Thickness	340 microns	13.4 mil	80
	660 microns	26.0 mil	120
Linear Mold Shrinkage, Flow	0.0070 - 0.011 cm/cm	0.0070 - 0.011 in/in
Linear Mold Shrinkage, Transverse	0.0070 - 0.011 cm/cm	0.0070 - 0.011 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	35.0 MPa	5080 psi
Elongation at Break	0.80 %	0.80 %
Tensile Modulus	9.70 GPa	1410 ksi
Charpy Impact Unnotched	1.50 J/cmÂ²	7.14 ft-lb/inÂ²
Charpy Impact, Notched	0.500 J/cmÂ²	2.38 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	170 Â°C	338 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	110 Â°C	230 Â°F
Vicat Softening Point	165 Â°C @Load 5.00 kg	329 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm

Processing Properties	Metric	English
Melt Temperature	250 - 270 Â°C	482 - 518 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	80.0 - 100 Â°C @Time 10800 sec	176 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa