Axion Polymers Axpoly® PS02 1010 Medium Impact Polystyrene

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer	Axion Polymers
Trade Name	Axpoly®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Axion Polymers Axpoly® PS02 1010 Medium Impact Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PS02 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS02 range of resin compounds are processed to a high purity and give consistent material properties during injection molding and sheet extrusion.Produced from 100% post-consumer raw materials, this product fits closely with Axion's other recycled resin grades and offers the same set of user benefits, including:Successfully replaces virgin resinHuge savings in CO2 impactAppeals to 'greener' customersCost-down on raw materialInformation provided by Axion Recycling

Physical Properties	Metric	English	Comments
Density	1.03 g/cc	0.0372 lb/in³	Typical; ISO 1183-1
	1.02 - 1.06 g/cc	0.0368 - 0.0383 lb/in³	Spec; ISO 1183-1
Particle Size	2000 - 4000 µm	2000 - 4000 µm	Pellet Size
	3000 µm	3000 µm	Typical
Melt Index of Compound	5.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C	5.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 392 °F	Spec
	7.0 g/10 min @Load 5.00 kg, Temperature 200 °C	7.0 g/10 min @Load 11.0 lb, Temperature 392 °F	Typical

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	18.0 - 27.0 MPa	2610 - 3920 psi	Spec; ISO 527-1/2
	23.0 MPa	3340 psi	Typical; ISO 527-1/2
Elongation at Break	35 %	35 %	Typical; ISO 527 - 1/2
	25 - 50 %	25 - 50 %	Spec; ISO 527 - 1/2
Izod Impact, Unnotched (ISO)	8.00 - 12.0 kJ/m²	3.81 - 5.71 ft-lb/in²	Spec; ISO 180
	10.0 kJ/m²	4.76 ft-lb/in²	Typical; ISO 180

Processing Properties	Metric	English	Comments
Moisture Content	0.17 %	0.17 %	Typical
	<= 0.25 %	<= 0.25 %	Spec