LATI Latene® AG7H K/30 PP Homopolymer, 30% Carbon Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latene® AG7H K/30 PP Homopolymer, 30% Carbon Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Carbon fiber. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa @Temperature 90.0 °C |
3630 psi @Temperature 194 °F |
|
| 35.0 MPa @Temperature 60.0 °C |
5080 psi @Temperature 140 °F |
||
| 55.0 MPa @Temperature 23.0 °C |
7980 psi @Temperature 73.4 °F |
||
| Elongation at Break | 0.90 % @Temperature 23.0 °C |
0.90 % @Temperature 73.4 °F |
|
| 1.3 % @Temperature 60.0 °C |
1.3 % @Temperature 140 °F |
||
| 2.3 % @Temperature 90.0 °C |
2.3 % @Temperature 194 °F |
||
| Tensile Modulus | 7.90 GPa @Temperature 90.0 °C |
1150 ksi @Temperature 194 °F |
|
| 11.0 GPa @Temperature 60.0 °C |
1600 ksi @Temperature 140 °F |
||
| 15.0 GPa @Temperature 23.0 °C |
2180 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 0.500 J/cm² | 2.38 ft-lb/in² | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 125 °C | 257 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |
| Vicat Softening Point | 160 °C @Load 5.00 kg |
320 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Plansee WRe26 Tungsten-Rhenium Alloy
- Pau Tai UNISTAB CH-1500 Organo Phosphite Chelator
- Plaskolite Optix® CP - 924 High Impact Grade Acrylic Resin
- MarkeTech Dermagrain 1200 Microcrystalline Alumina for Microdermabrasion
- Shakespeare Resistat® F901 R080 Nylon 66 Monofilament
- Arlon R35928R025 0.025" (0.635 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Beijing Ranger Chem PBT-201-G30 202 Environmental Protection Flame Retarding FR PBT
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR Thanecure ZM
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N330 Filler
Copyright © lookpolymers.com All Rights Reserved