LATI Latene® 22H2 MX/25 PP Homopolymer, Heat Stabilized

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer LATI
Trade Name Latene®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Latene® 22H2 MX/25 PP Homopolymer, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polypropylene homopolymer (PPh) based compound. Heat stabilized. Special mineral filler. Very good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
Linear Mold Shrinkage, Flow 0.011 - 0.014 cm/cm
0.011 - 0.014 in/in
Linear Mold Shrinkage, Transverse 0.0115 - 0.0145 cm/cm
0.0115 - 0.0145 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 18.0 MPa
2610 psi
Elongation at Break >= 100 %
<br>@Temperature 23.0 °C
 >= 100 %
<br>@Temperature 73.4 °F
>= 100 %
<br>@Temperature 60.0 °C
 >= 100 %
<br>@Temperature 140 °F
>= 100 %
<br>@Temperature 90.0 °C
 >= 100 %
<br>@Temperature 194 °F
Elongation at Yield 6.0 %
<br>@Temperature 23.0 °C
 6.0 %
<br>@Temperature 73.4 °F
8.5 %
<br>@Temperature 60.0 °C
 8.5 %
<br>@Temperature 140 °F
9.0 %
<br>@Temperature 90.0 °C
 9.0 %
<br>@Temperature 194 °F
Tensile Modulus 0.650 GPa
<br>@Temperature 90.0 °C
 94.3 ksi
<br>@Temperature 194 °F
1.10 GPa
<br>@Temperature 60.0 °C
 160 ksi
<br>@Temperature 140 °F
2.60 GPa
<br>@Temperature 23.0 °C
 377 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²
<br>@Temperature -20.0 °C
 7.14 ft-lb/in²
<br>@Temperature -4.00 °F
6.50 J/cm²
<br>@Temperature 23.0 °C
 30.9 ft-lb/in²
<br>@Temperature 73.4 °F
Charpy Impact, Notched 0.100 J/cm²
<br>@Temperature -20.0 °C
 0.476 ft-lb/in²
<br>@Temperature -4.00 °F
0.350 J/cm²
<br>@Temperature 23.0 °C
 1.67 ft-lb/in²
<br>@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 95.0 °C
<br>@Load 5.00 kg
 203 °F
<br>@Load 11.0 lb
Flammability, UL94 2.00
<br>@Thickness 1.50 mm
 2.00
<br>@Thickness 0.0591 in
2.00
<br>@Thickness 0.750 mm
 2.00
<br>@Thickness 0.0295 in
Oxygen Index 24 %
24 %
Glow Wire Test 750 °C
<br>@Thickness 1.00 mm
 1380 °F
<br>@Thickness 0.0394 in
 GWFI/GWT
750 °C
<br>@Thickness 2.00 mm
 1380 °F
<br>@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 200 - 240 °C
392 - 464 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 80.0 - 90.0 °C
<br>@Time 10800 sec
 176 - 194 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa