Techmer ES Luriblend® TPX-PA6-95002
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® TPX-PA6-95002.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % @Time 86400 sec |
0.70 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0019 cm/cm @Thickness 3.17 mm |
0.0019 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 78 | 78 | ASTM D785 |
| Tensile Strength | 47.6 MPa | 6900 psi | ASTM D638 |
| Elongation at Yield | 19 % | 19 % | ASTM D638 |
| Flexural Yield Strength | 76.5 MPa | 11100 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm |
1.30 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 10.1 J/cm @Thickness 3.17 mm |
19.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 97.2 µm/m-°C | 54.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Fine Organics FINALUX G 728 Lubricant Additive
- Isoflon Tisoflon® 6 AD EXTRA SMOOTH Polytetrafluoroethylene Coated Glass Fabric
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC
- Trelleborg Horda Cable E8502 Strippable Semiconductive Shielding
- Polyram RamTal PM8515 Acetal, High impact
- A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6
- Bohler-Uddeholm UDDEHOLM Caldie Plastic Mold Tool Steel
- C.O.I.M. DIEXTER® G173 Polyol Polyester
- Aaron Industries AAROLENE® ARPE HD 300-2 High Density Polyethylene Compounded Resin
- Axiall 19732 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved