LATI Latan 13 S/15 POM, 15% Glass Bead Reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled |
| Manufacturer | LATI |
| Trade Name | Latan |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latan 13 S/15 POM, 15% Glass Bead Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyoxymethylene (POM) based compound. Glass beads. Medium viscosity. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0195 - 0.0225 cm/cm | 0.0195 - 0.0225 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0195 - 0.022 cm/cm | 0.0195 - 0.022 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa @Temperature 60.0 °C |
4350 psi @Temperature 140 °F |
|
| 45.0 MPa @Temperature 23.0 °C |
6530 psi @Temperature 73.4 °F |
||
| Elongation at Break | 15 % @Temperature 23.0 °C |
15 % @Temperature 73.4 °F |
|
| 75 % @Temperature 60.0 °C |
75 % @Temperature 140 °F |
||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| Elongation at Yield | 8.0 % @Temperature 23.0 °C |
8.0 % @Temperature 73.4 °F |
|
| 8.0 % @Temperature 60.0 °C |
8.0 % @Temperature 140 °F |
||
| 9.0 % @Temperature 90.0 °C |
9.0 % @Temperature 194 °F |
||
| Tensile Modulus | 1.20 GPa @Temperature 90.0 °C |
174 ksi @Temperature 194 °F |
|
| 2.00 GPa @Temperature 60.0 °C |
290 ksi @Temperature 140 °F |
||
| 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | |
| Vicat Softening Point | 150 °C @Load 5.00 kg |
302 °F @Load 11.0 lb |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3740 TPE, PP Overmold or Standalone use
- Solvay Specialty Polymers Amodel® A-1145 DW Polyphthalamide (PPA), 45% Glass Fiber
- Borealis LE0595-07 Polyethylene Compound, Crosslinkable, Semiconductive
- Vyncolit Neopreg Kinel® SK80 L8G Glass Fiber Reinforced Molding Compound
- Polyram PlusTek RA102 Nylon 6.6, General Purpose
- Epoxy Technology EPO-TEK® 310M-T Flexible Epoxy
- ConocoPhillips IGL-9 Enclosed Gear Lubricant ISO 680, AGMA Number 8EP
- Atom Adhesives AA-BOND 2103 Epoxy Adhesive
- DuPont Performance Polymers Zytel® 77G43L NC010 Nylon 612 (Unverified Data**)
- ExxonMobil Escorene® LD 783.ND Molding, extrusion and compounding resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved