LATI Latamid SP2 H2 G/35 PA 6.12, 35% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Glass Fiber Filler
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Latamid SP2 H2 G/35 PA 6.12, 35% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polyamide 6.12 (PA6.12) based compound. Heat stabilized. Glass fibers. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
<br>@Temperature 150 °C
 8700 psi
<br>@Temperature 302 °F
75.0 MPa
<br>@Temperature 120 °C
 10900 psi
<br>@Temperature 248 °F
90.0 MPa
<br>@Temperature 90.0 °C
 13100 psi
<br>@Temperature 194 °F
105 MPa
<br>@Temperature 60.0 °C
 15200 psi
<br>@Temperature 140 °F
145 MPa
<br>@Temperature 23.0 °C
 21000 psi
<br>@Temperature 73.4 °F
Elongation at Break 3.6 %
<br>@Temperature 23.0 °C
 3.6 %
<br>@Temperature 73.4 °F
4.7 %
<br>@Temperature 60.0 °C
 4.7 %
<br>@Temperature 140 °F
5.4 %
<br>@Temperature 90.0 °C
 5.4 %
<br>@Temperature 194 °F
6.0 %
<br>@Temperature 120 °C
 6.0 %
<br>@Temperature 248 °F
6.8 %
<br>@Temperature 150 °C
 6.8 %
<br>@Temperature 302 °F
Tensile Modulus 3.20 GPa
<br>@Temperature 150 °C
 464 ksi
<br>@Temperature 302 °F
3.90 GPa
<br>@Temperature 120 °C
 566 ksi
<br>@Temperature 248 °F
5.60 GPa
<br>@Temperature 90.0 °C
 812 ksi
<br>@Temperature 194 °F
6.50 GPa
<br>@Temperature 60.0 °C
 943 ksi
<br>@Temperature 140 °F
9.30 GPa
<br>@Temperature 23.0 °C
 1350 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 9.50 J/cm²
45.2 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Vicat Softening Point 210 °C
<br>@Load 5.00 kg
 410 °F
<br>@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 250 - 280 °C
482 - 536 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 - 100 °C
<br>@Time 10800 sec
 176 - 212 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa