Victrex® WG102™ Polyaryletherketone

Category	Polymer , Thermoplastic , Polyketone
Manufacturer	Victrex
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Victrex® WG102™ Polyaryletherketone.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliantWG102 does not contain polyetrafluoroethylene (PTFE) or other halogenated additivesTypical Application Areas: Higher temperature tribological applications for high strength and stiffness. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information provided by Victrex

Physical Properties	Metric	English	Comments
Density	1.44 g/cc	0.0520 lb/in³	Crystalline; ISO 1183
Viscosity	575000 cP @Temperature 400 °C	575000 cP @Temperature 752 °F	Melt; ISO 11443
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	410°C nozzle, 190°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	410°C nozzle, 190°C tool; ISO 294-4
Spiral Flow	36.0 cm @Thickness 3.00 mm	14.2 in @Thickness 0.118 in	410°C nozzle, 190°C tool; Victrex
	85.0 cm @Thickness 1.00 mm	33.5 in @Thickness 0.0394 in	410°C nozzle, 190°C tool; Victrex

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	86	86	ISO 868
Tensile Strength at Break	55.0 MPa @Temperature 275 °C	7980 psi @Temperature 527 °F	ISO 527
	85.0 MPa @Temperature 175 °C	12300 psi @Temperature 347 °F	ISO 527
	130 MPa @Temperature 125 °C	18900 psi @Temperature 257 °F	ISO 527
	195 MPa @Temperature 23.0 °C	28300 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	2.0 %	2.0 %	ISO 527
Tensile Modulus	19.5 GPa	2830 ksi	ISO 527
Flexural Strength	75.0 MPa @Temperature 275 °C	10900 psi @Temperature 527 °F	ISO 178
	145 MPa @Temperature 175 °C	21000 psi @Temperature 347 °F	ISO 178
	220 MPa @Temperature 125 °C	31900 psi @Temperature 257 °F	ISO 178
	290 MPa @Temperature 23.0 °C	42100 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	17.0 GPa	2470 ksi	ISO 178
Compressive Strength	55.0 MPa @Temperature 250 °C	7980 psi @Temperature 482 °F	ISO 604
	75.0 MPa @Temperature 200 °C	10900 psi @Temperature 392 °F	ISO 604
	145 MPa @Temperature 120 °C	21000 psi @Temperature 248 °F	ISO 604
	250 MPa @Temperature 23.0 °C	36300 psi @Temperature 73.4 °F	ISO 604
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	ISO 180/A
Izod Impact, Unnotched (ISO)	40.0 kJ/m²	19.0 ft-lb/in²	ISO 180/U
Charpy Impact Unnotched	3.50 J/cm²	16.7 ft-lb/in²	ISO 179/1eA
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	ISO 179/1U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	9.00 µm/m-°C	5.00 µin/in-°F	Below Tg; ISO 11359
	10.0 µm/m-°C	5.56 µin/in-°F	Above Tg; ISO 11359
CTE, linear, Transverse to Flow	35.0 µm/m-°C	19.4 µin/in-°F	Average below Tg; ISO 11359
	90.0 µm/m-°C	50.0 µin/in-°F	Average above Tg; ISO 11359
Thermal Conductivity	1.30 W/m-K	9.02 BTU-in/hr-ft²-°F	Average; ISO/CD 22007-4
	2.20 W/m-K	15.3 BTU-in/hr-ft²-°F	Along flow; ISO 22007-4
Melting Point	373 °C	703 °F	ISO 11357
Deflection Temperature at 1.8 MPa (264 psi)	367 °C	693 °F	ISO 75-f
Glass Transition Temp, Tg	152 °C	306 °F	Onset; ISO 11357
	180 °C	356 °F	Midpoint; ISO 11357

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+7 ohm-cm	1.00e+7 ohm-cm	1V; IEC 60093

Processing Properties	Metric	English	Comments
Processing Temperature	<= 100 °C	<= 212 °F	Hopper Temperature
Nozzle Temperature	410 °C	770 °F
Zone 1	390 °C	734 °F
Zone 2	395 °C	743 °F
Zone 3	400 °C	752 °F
Zone 4	405 °C	761 °F
Mold Temperature	190 - 215 °C	374 - 419 °F
	<= 250 °C	<= 482 °F
Dry Time	3 hour @Temperature 150 °C	3 hour @Temperature 302 °F
	5 hour @Temperature 120 °C	5 hour @Temperature 248 °F

Descriptive Properties	Value	Comments
Color	Black
Gate	> 2mm or 0.5 x part thickness
Runner	Die/nozzle > 3mm, manifold > 3.5mm