LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Toughened. Glass fibers. High impact resistance. Good impact resistance even at low temperature.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Linear Mold Shrinkage, Flow 0.0055 - 0.0085 cm/cm
0.0055 - 0.0085 in/in
Linear Mold Shrinkage, Transverse 0.0105 - 0.0135 cm/cm
0.0105 - 0.0135 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa

@Temperature 150 °C
 5080 psi

@Temperature 302 °F
45.0 MPa

@Temperature 120 °C
 6530 psi

@Temperature 248 °F
50.0 MPa

@Temperature 90.0 °C
 7250 psi

@Temperature 194 °F
70.0 MPa

@Temperature 60.0 °C
 10200 psi

@Temperature 140 °F
100 MPa

@Temperature 23.0 °C
 14500 psi

@Temperature 73.4 °F
Elongation at Break 4.0 %

@Temperature 23.0 °C
 4.0 %

@Temperature 73.4 °F
6.5 %

@Temperature 60.0 °C
 6.5 %

@Temperature 140 °F
10 %

@Temperature 150 °C
 10 %

@Temperature 302 °F
12 %

@Temperature 90.0 °C
 12 %

@Temperature 194 °F
12 %

@Temperature 120 °C
 12 %

@Temperature 248 °F
Elongation at Yield 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
4.0 %

@Temperature 60.0 °C
 4.0 %

@Temperature 140 °F
7.0 %

@Temperature 150 °C
 7.0 %

@Temperature 302 °F
7.5 %

@Temperature 90.0 °C
 7.5 %

@Temperature 194 °F
8.0 %

@Temperature 120 °C
 8.0 %

@Temperature 248 °F
Tensile Modulus 1.50 GPa

@Temperature 150 °C
 218 ksi

@Temperature 302 °F
1.70 GPa

@Temperature 120 °C
 247 ksi

@Temperature 248 °F
2.10 GPa

@Temperature 90.0 °C
 305 ksi

@Temperature 194 °F
3.70 GPa

@Temperature 60.0 °C
 537 ksi

@Temperature 140 °F
4.60 GPa

@Temperature 23.0 °C
 667 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.50 J/cm²

@Temperature -20.0 °C
 26.2 ft-lb/in²

@Temperature -4.00 °F
6.50 J/cm²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.400 J/cm²

@Temperature -20.0 °C
 1.90 ft-lb/in²

@Temperature -4.00 °F
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Vicat Softening Point 235 °C

@Load 5.00 kg
 455 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa