Cossa Polimeri ESTABLEND 6500 F Polycarbonate ABS Blend

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Cossa Polimeri S.r.L.
Trade Name	ESTABLEND
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cossa Polimeri ESTABLEND 6500 F Polycarbonate ABS Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polycarbonate and Acrylonitrile Butadiene Styrene blendHigh melt flow rate, good thermal resistance, good impact resistance, excellent processability, good surface appearanceInformation provided by Cossa Polimeri S.r.l.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ASTM D 792
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ASTM D 955
Melt Flow	30 g/10 min @Load 5.00 kg, Temperature 260 °C	30 g/10 min @Load 11.0 lb, Temperature 500 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	47.0 MPa	6820 psi	ASTM D 638
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D 638
Elongation at Break	45 %	45 %	ASTM D 638
Flexural Modulus	2.30 GPa	334 ksi	ASTM D 790
Izod Impact, Notched	4.50 J/cm @Temperature 0.000 °C	8.43 ft-lb/in @Temperature 32.0 °F	ASTM D 638
	5.00 J/cm @Temperature 23.0 °C	9.37 ft-lb/in @Temperature 73.4 °F	ASTM D 256

Thermal Properties	Metric	English	Comments
Vicat Softening Point	125 °C @Load 5.00 kg	257 °F @Load 11.0 lb	50°C/hr; ASTM D 1525
	135 °C @Load 0.999 kg	275 °F @Load 2.20 lb	50°C/hr; ASTM D 1525
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in
Glow Wire Test	750 °C	1380 °F	I.E.C. 695-2-1