LATI Latamid 6 H2 G/20-V0 PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2 G/20-V0 PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0065 cm/cm
0.0040 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0080 cm/cm
0.0055 - 0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 10.0 MPa

@Temperature 150 °C
 1450 psi

@Temperature 302 °F
20.0 MPa

@Temperature 120 °C
 2900 psi

@Temperature 248 °F
25.0 MPa

@Temperature 90.0 °C
 3630 psi

@Temperature 194 °F
40.0 MPa

@Temperature 60.0 °C
 5800 psi

@Temperature 140 °F
55.0 MPa

@Temperature 23.0 °C
 7980 psi

@Temperature 73.4 °F
Elongation at Break 1.0 %

@Temperature 23.0 °C
 1.0 %

@Temperature 73.4 °F
1.2 %

@Temperature 60.0 °C
 1.2 %

@Temperature 140 °F
2.0 %

@Temperature 90.0 °C
 2.0 %

@Temperature 194 °F
2.5 %

@Temperature 120 °C
 2.5 %

@Temperature 248 °F
5.0 %

@Temperature 150 °C
 5.0 %

@Temperature 302 °F
Elongation at Yield 1.7 %

@Temperature 90.0 °C
 1.7 %

@Temperature 194 °F
2.0 %

@Temperature 120 °C
 2.0 %

@Temperature 248 °F
2.5 %

@Temperature 150 °C
 2.5 %

@Temperature 302 °F
Tensile Modulus 2.40 GPa

@Temperature 150 °C
 348 ksi

@Temperature 302 °F
3.00 GPa

@Temperature 120 °C
 435 ksi

@Temperature 248 °F
3.60 GPa

@Temperature 90.0 °C
 522 ksi

@Temperature 194 °F
6.50 GPa

@Temperature 60.0 °C
 943 ksi

@Temperature 140 °F
8.00 GPa

@Temperature 23.0 °C
 1160 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
1.50 J/cm²

@Temperature -20.0 °C
 7.14 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
0.400 J/cm²

@Temperature -20.0 °C
 1.90 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 85.0 °C
185 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
Vicat Softening Point 210 °C

@Load 5.00 kg
 410 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 29 %
29 %
Glow Wire Test 775 °C

@Thickness 1.00 mm
 1430 °F

@Thickness 0.0394 in
 GWIT
800 °C

@Thickness 2.00 mm
 1470 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 300 V
300 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: