LATI LATAN 13 K/30 30% Carbon Fiber Reinforced Polyoxymethylene Copolymer (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LATAN 13 K/30 30% Carbon Fiber Reinforced Polyoxymethylene Copolymer (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gears, cams, bushings, and other parts for the electromechanical, hydraulic, and automotive sectors, and others). A good resistance to hydrolysis makes it usable in hot water up to 80°-90°C. Basic Latan versions featuring low or high flowability are available, as well as an elastomer modified version to improve product toughness.Specific Notes for this Material: 30% carbon fiber; very high rigidity; low specific resistivity; good self-lubricating properties.Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
at 23°C; ISO 62
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
LATI
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
LATI
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ASTM D785
Tensile Strength, Ultimate 85.0 MPa
12300 psi
ISO 527
Flexural Modulus 17.0 GPa
2470 ksi
ASTM D790
Izod Impact, Notched 0.380 J/cm

@Temperature -20.0 °C
0.712 ft-lb/in

@Temperature -4.00 °F
ASTM D256
0.380 J/cm

@Temperature 23.0 °C
0.712 ft-lb/in

@Temperature 73.4 °F
ASTM D256
0.400 J/cm

@Temperature -40.0 °C
0.749 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Charpy Impact Unnotched 0.900 J/cm²

@Temperature -20.0 °C
4.28 ft-lb/in²

@Temperature -4.00 °F
DIN 53453
0.900 J/cm²

@Temperature -40.0 °C
4.28 ft-lb/in²

@Temperature -40.0 °F
DIN 53453
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
DIN 53453
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 168 °C
334 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
ASTM D648
Vicat Softening Point 163 °C
325 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Oxygen Index 18 %
18 %
ISO 4589
Electrical Properties Metric English Comments
Surface Resistance 1000 ohm
1000 ohm
IEC 93
Dielectric Strength 3.00 kV/mm

@Thickness 2.00 mm
76.2 kV/in

@Thickness 0.0787 in
IEC 243-1
Comparative Tracking Index <= 100 V
<= 100 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 180 - 210 °C
356 - 410 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Not essential, temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Not essential, drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Heat Resistance - Ball Test (125°C) Y
IEC 335
Heat Resistance - Ball Test (165°C) N
IEC 335
Injection Speed medium
Needle Burner Test N
1.47 mm
N
3.05 mm