Asahi Kasei Thermylene® P-25FG-3809 25% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P-25FG-3809 25% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 112 MPa | 16300 psi | ASTM D790 |
| Flexural Modulus | 4.34 GPa | 630 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0591 in thickness |
Users viewing this material also viewed the following:
- Mearthane Durethaneâ„¢ C 70D Polyurethane
- Washington Penn Medium Impact Copolymer 10% Calcium Carbonate Filled
- Eagle Brass 762 Nickel Silver 12%, 1/4 Hard
- ExxonMobil Bicor™ 35MB666 OPP Film
- Arlon R33682C045 0.045" (1.14 mm) Cured Silicone Rubber with Fiberglass Substrate
- ExxonMobil Label-Lyte® 612 LL-112 Clear OPP Overlaminate
Copyright © lookpolymers.com All Rights Reserved