- Kolon SPESIN® KP213G30SB3 Glass Fiber Reinforced PBT Compound Resin
Kolon SPESIN® KP213G30SB3 Glass Fiber Reinforced PBT Compound Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | SPESIN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon SPESIN® KP213G30SB3 Glass Fiber Reinforced PBT Compound Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
G/F 30% reinforcedApplications: Ignition coil bobbinsInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.010 cm/cm | 0.0050 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 108 MPa | 15700 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 177 MPa | 25700 psi | ASTM D790 |
| Flexural Modulus | 6.276 GPa | 910.3 ksi | ASTM D790 |
| Izod Impact, Notched | 1.67 J/cm | 3.13 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Melting Point | 224 °C | 435 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.2 | 3.2 | ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8512SB (UF) Synthetic Oil
- North Wood Plastics 60 PP + UNIFILL (40% Wood Fiber)
- Resinlab® CYNERGY CA6105 Adhesive
- LG Chemical i-Pentane
- Mikro-Technik Reproflon PTFE
- TIMCAL TIMREX® LSG6 Natural Graphite
- A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Dow Corning 7096 CLEAR SEALANT
- Chi Mei Wonderlite® PC-175 Polycarbonate
- BNZ Materials BNZP-26 Insulating Firebrick (French Grade)
Copyright © lookpolymers.com All Rights Reserved