Owens Corning Glass Fiber Reinforced Acetal, 25 wt.% glass
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Owens Corning |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Owens Corning Glass Fiber Reinforced Acetal, 25 wt.% glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, Owens Corning.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ASTM D792 |
| Water Absorption | 0.29 % | 0.29 % | 24 hrs.; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 79 | 79 | ASTM D785 |
| Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Modulus of Elasticity | 8.62 GPa | 1250 ksi | ASTM D638 |
| Flexural Strength | 190 MPa | 27600 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Strength | 120 MPa | 17400 psi | ASTM D695 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.46 µm/m-°C @Temperature 20.0 °C |
4.70 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.12 @Frequency 60 Hz |
4.12 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 22.8 kV/mm | 580 kV/in | ASTM D149 |
| Arc Resistance | 142 sec | 142 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Oceanchem Group Triphenyl Phosphate (TPP)
- Mallard Creek Polymers ROVENE® 4076 SBR Latex
- Indium Corp. Indalloy® 244 99.3Sn/0.7Cu Lead-Free Solder Alloy
- Loxim 330 01HSL Nylon 6
- Loctite® 277 High Strength Threadlocker
- Clariant Renol PA111G50 Nylon 66, 50% Glass Fiber
- ATI Allvac® 6-2-4-6 Titanium Alloy, Heat Treatment: 885°C (1625°F) + Age
- ATI Allegheny Ludlum Stainless Steel Type 201L, 30% Cold Work (UNS S20103)
Copyright © lookpolymers.com All Rights Reserved