Arkema Group Rilsan® AMN G8 TLD Nylon 12, Graphite Filled (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Graphite Filled
Manufacturer	Arkema
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® AMN G8 TLD Nylon 12, Graphite Filled (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation ISO 1874-PA12,MHLS,14-010,CD05Rigid grade with graphite filler for injection molding. Available colors: steel gray. Light and heat stabilized. Mold-release agent.Low friction coefficient. No need of lubricant. Good mechanical properties. Easy filling of the mold due to its well adapted viscosity. Low shrinkage: include 1% on average for the design of the mold. Very good dimensional stability (low moisture absorption). Higher rate of production.Example applications: Moving mechanical parts.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English
Density	1.02 g/cc	0.0368 lb/in³
Water Absorption	1.6 %	1.6 %
Melt Flow	61.5 g/10 min @Load 2.16 kg, Temperature 235 °C	61.5 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	45.0 MPa	6530 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	10 %	10 %	50 mm/min
Tensile Modulus	1.52 GPa	220 ksi	1 mm/min
Charpy Impact Unnotched	NB	NB
	NB	NB	Low Temp
Charpy Impact, Notched	0.410 J/cm²	1.95 ft-lb/in²
	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Melting Point	174 °C	345 °F	10°C/min
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.10 mm	HB @Thickness 0.122 in

Electrical Properties	Metric	English	Comments
Dissipation Factor	0.000332 @Frequency 1e+6 Hz	0.000332 @Frequency 1e+6 Hz
	0.00045 @Frequency 100 Hz	0.00045 @Frequency 100 Hz