Kingfa PC-S809 Modified PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa PC-S809 Modified PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Good mechanical propertiesSuper high impact strengthGood weather resistanceHigh glossGood processing propertiesStress cracking propertiesApplications:OA and IT partsAutomobile accessoriesElectrical and electronic partsSwitch and plugHousehold applianceInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc @Temperature 23.0 °C |
1.19 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Temperature 23.0 °C |
0.0050 - 0.0070 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50mm/min; ASTM D638 |
| Elongation at Break | >= 60 % | >= 60 % | 50mm/min; ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
5.99 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| 6.20 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
11.6 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 300 °C | <= 572 °F | |
| Rear Barrel Temperature | 230 - 270 °C | 446 - 518 °F | Start Point: 250°C |
| Middle Barrel Temperature | 235 - 280 °C | 455 - 536 °F | Start Point: 260°C |
| Front Barrel Temperature | 240 - 290 °C | 464 - 554 °F | Start Point: 270°C |
| Melt Temperature | 230 - 280 °C | 446 - 536 °F | Start Point: 255°C |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Start Point: 60°C |
| Drying Temperature | 105 - 115 °C @Time 10800 - 14400 sec |
221 - 239 °F @Time 3.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.300 - 1.00 MPa | 43.5 - 145 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | 60-90% | |
| Weather Resistance (delta E) | ASTM D4459; 200hr xenon lamp |
Users viewing this material also viewed the following:
- Poco Graphite AXF-5F Biomedical Grade Graphite
- PolyOne Bergamid™ B65 G/Mi20 UF grey LS Polyamide 6 (Nylon 6)
- Fiberfil® J-60/20/E Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
- Global PC/ABS-1216 General Purpose Polycarbonate/ABS Alloy
- Sax Polymers SAXAMID 126 Nylon 6, Injection Molding Grade
- Borealis RJ370MO Polypropylene, Transparent Random Copolymer
- A. Schulman POLYBATCH™ Green 3012E Concentrate Based In Polyethylene
- A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6
- A. Schulman POLYBATCH™ Green 3251V Concentrate Based In Polyethylene
- EMS-Grivory Grivory® GVS-5H nat PA*-GF50
Copyright © lookpolymers.com All Rights Reserved