Kingfa JH720 G50 50% Glass Fiber Reinforced PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 50% Glass Filled |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa JH720 G50 50% Glass Fiber Reinforced PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Excellent balance propertiesSuper high stiffnessHigh hardnessGood size stabilitySuper high mechanical strengthApplications:Imaging equipment shellOA body frameElectrical equipmentComputer plug partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc @Temperature 23.0 °C |
1.51 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm @Temperature 23.0 °C |
0.0010 - 0.0020 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ASTM D785 |
| Tensile Strength at Break | 125 MPa | 18100 psi | 10mm/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | 10mm/min; ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.06 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Unnotched | 5.90 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
11.1 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | 1.6mm; ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 295 °C | <= 563 °F | |
| Rear Barrel Temperature | 240 - 280 °C | 464 - 536 °F | Start Point: 265°C |
| Middle Barrel Temperature | 250 - 290 °C | 482 - 554 °F | Start Point: 275°C |
| Front Barrel Temperature | 260 - 295 °C | 500 - 563 °F | Start Point: 280°C |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Start Point: 270°C |
| Mold Temperature | 100 - 140 °C | 212 - 284 °F | Start Point: 110°C |
| Drying Temperature | 110 - 120 °C @Time 10800 - 14400 sec |
230 - 248 °F @Time 3.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.300 - 1.00 MPa | 43.5 - 145 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Glass Fiber Content (%) | 50 | |
| Injection Speed | 60-90% |
Users viewing this material also viewed the following:
- Inno-Comp INNOPOL® CS 1-3000 B DEL Polypropylene Homopolymer
- Lucas-Milhaupt 60 Sn-40 Pb Tin/ Silver Solder
- H.C. Starck Amperit® 558.088 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
- Sylvin Technologies 9940-95 Natural PVC Molding Compound
- Borealis EE002AE Polypropylene Elastomer Modified
- Zeon Chemicals Sivic® Z8901 Polyblend Nitrile Elastomer
- DuPont Teijin Films Melinex® FRP Polyester Film, 92 Gauge
- Fainplast Compounds GA 87/4 Flexible PVC, Flame Retardant Sheathing
- Axiall 10852 Wire & Cable Flexible PVC
- 3M 9471FL Adhesive Transfer Tape with 300LSE Adhesive
Copyright © lookpolymers.com All Rights Reserved