Kingfa JH720 G10 10% Glass Fiber Reinforced PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa JH720 G10 10% Glass Fiber Reinforced PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:High mechanical strengthGood size stabilityGood surfaceSuitable for exact moldingApplications:Exact mechanism partsPrinter, photocopies, scanner cabinetComputer plug partsCD-ROM, DVDElectrical equipment partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc @Temperature 23.0 °C |
1.26 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm @Temperature 23.0 °C |
0.0030 - 0.0050 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 84 | 84 | ASTM D785 |
| Tensile Strength at Break | 76.0 MPa | 11000 psi | 10mm/min; ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | 10mm/min; ASTM D638 |
| Flexural Strength | 112 MPa | 16200 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 4.35 GPa | 631 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.21 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Unnotched | 5.70 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
10.7 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 6.40 mm |
280 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | 1.6mm; ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 290 °C | <= 554 °F | |
| Rear Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Start Point: 255°C |
| Middle Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Start Point: 260°C |
| Front Barrel Temperature | 250 - 285 °C | 482 - 545 °F | Start Point: 270°C |
| Melt Temperature | 245 - 270 °C | 473 - 518 °F | Start Point: 250°C |
| Mold Temperature | 80.0 - 130 °C | 176 - 266 °F | Start Point: 90°C |
| Drying Temperature | 110 - 120 °C @Time 10800 - 14400 sec |
230 - 248 °F @Time 3.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Glass Fiber Content (%) | 10 | |
| Injection Speed | 60-90% |
Users viewing this material also viewed the following:
- NYCOA 2037 15% Glass Filled Nylon 6
- Plaskolite West Optix® CA - 927 High Impact Acrylic Resin
- PolyOne Geon™ Vinyl Dry Blend E0916 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Phillips 66 COPYLENE® CR350CS-01 Polypropylene Random Copolymer
- Kazanorgsintez E-1 Petroleum Resin
- A. Schulman POLYBATCH™ Red LL50283/3 Concentrate Based In LLDPE
- Wellman Wellamid® WE1359 25% Glass Sphere Filled, Toughened Nylon 66
- Alcoa QC-10® Aluminum Mold Alloy
- American Elements Ruthenium Nanoparticles
- Advanced Polymer Alloys Alcryn® 3075 NC Melt Processable Rubber
Copyright © lookpolymers.com All Rights Reserved