Inno-Comp INNOPOL® CS 1-7120 AP 20% Talc Filled Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-7120 AP 20% Talc Filled Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 1-7120 is a 20 % talc-filled polypropylene homopolymer compound. This grade is available in natural and custom colored form.INNOPOL® CS 1-7120 is recommended for extrusion of sheets and profiles, where one of the required properties is good stiffness.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Melt Flow | 0.80 g/10 min @Load 5.00 kg, Temperature 230 °C |
0.80 g/10 min @Load 11.0 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.80 J/cm² @Temperature -20.0 °C |
8.57 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eU |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 0.350 J/cm² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| 190 - 260 °C | 374 - 500 °F | Injection | |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| 190 - 260 °C | 374 - 500 °F | Injection | |
| Front Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| 190 - 260 °C | 374 - 500 °F | Injection | |
| Die Temperature | 190 - 220 °C | 374 - 428 °F | Extrusion |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Extrusion |
| 240 - 260 °C | 464 - 500 °F | Injection | |
| Mold Temperature | 15.0 - 50.0 °C | 59.0 - 122 °F | |
| Moisture Content | <= 0.070 % | <= 0.070 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP-H TD 20 | ISO 1043 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 203 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific)
- SSAB Tunnplat Docol® 600DL High-strength Steel
- Techmer ES Luriblend® PC CF15 TL6 BK 15% Carbon Filled
- SABIC Innovative Plastics LNP THERMOCOMP WFB44 PBT (Europe-Africa-Middle East)
- EMS-Griltech Grilon® BM 25R Nylon 6 Monofilament (Medium-Set)
- Clariant Renol PA123G13 Nylon 66, 13% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated
- Advanced Polymer Alloys Alcryn® 4680 NC Melt Processable Rubber
- BASF Ultradur® B 4300 G10 50% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved