| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® PG 298.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features:UnfilledPlatableSuitable processing methods:Injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Water Absorption | 0.30 % | 0.30 % | |
| Melt Flow | 19 g/10 min @Load 10.0 kg, Temperature 220 °C |
19 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
| Elongation at Break | 30 % | 30 % | Nominal |
| Elongation at Yield | 2.7 % | 2.7 % | |
| Tensile Modulus | 2.77 GPa | 402 ksi | |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | |
| Vicat Softening Point | 97.8 °C | 208 °F | 50°C/h 50N |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL Recognized |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL Recognized |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | |
| Surface Resistance | 3.00e+14 ohm | 3.00e+14 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection Molding |
| Mold Temperature | 60.0 °C | 140 °F | Injection Molding |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | |
| Injection Pressure | 55.0 MPa | 7980 psi |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CR120CL Polypropylene, Random Copolymer, Clarified, Lubricated
- Spartech E65350 General Purpose PVC
- Teknor Apex Flexalloy® 9609-80 Polyvinyl Chloride Compound
- C.O.I.M. LARIPUR® LPR2203-93A Seal Grade TPU
- 3M Scotch® 2460 Ultimate Paint Edge Masking Tape
- Chem Polymer Chemlon 125-15 MG Nylon 66, 25% Mineral/15% Glass Fiber Reinforced
- A. Schulman PP 1227E-01 Polypropylene High-Impact Polypropylene
Copyright © lookpolymers.com All Rights Reserved