Isoflon PA 6.6 Polyamide 6.6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Isoflon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Isoflon PA 6.6 Polyamide 6.6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General use for mechanical partsGood heat resistanceEasy to useHigh moisture regainInformation provided by Isoflon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | DIN 53479 |
| Water Absorption | 2.5 % | 2.5 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength | 80.0 MPa | 11600 psi | DIN 53455 |
| Elongation at Break | 25 % | 25 % | DIN 53455 |
| Tensile Modulus | 3.30 GPa | 479 ksi | DIN 53457 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 85.0 µm/m-°C | 47.2 µin/in-°F | DIN 52328 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 255 °C | 491 °F | DIN 53736 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; DIN 52612 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous; DIN 52612 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | DIN 53482 |
| Dielectric Constant | 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
DIN 53483 |
| Dielectric Strength | 18.0 - 27.0 kV/mm | 457 - 686 kV/in | DIN 53481 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Nat./Black |
Users viewing this material also viewed the following:
- Quadrant EPP Fluorosint® MT-01 PTFE + additives, enhanced grade, compression moulded (ISO Data)
- Hyosung Topilene HJ700 PP
- Mitsui UNISTOLEâ„¢ R-100K Polyolefinic Primer/ Adhesive
- Samsung Cheil Industries Infino® NH-3402F PC, 40% Glass Filled FR
- Saint-Gobain Chemfab® 1584N PTFE Coated Fiberglass Conveyor Belting
- A. Schulman POLYBATCH™ White 8750 Concentrate Based In HDPE
- A. Schulman POLYBLAK™ 3225 Superior Black Color Concentrate, 50% Carbon Black Based In PP Homopolymer
- Ensinger Tecapeek® XP-118 Compression Molded PEEK Compound, 20% Fiberglass with 5% PTFE
- 3M 3000WT Fire Barrier Water Tight Sealant
- ExxonMobil AA Mobil DTE Oil Double Letter Series
Copyright © lookpolymers.com All Rights Reserved