Plenco 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound  (discontinued **)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Mineral/Flock Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plaslok 306 is a two-stage, mineral and flock-filled phenolic molding compound designed to have the heat resistant characteristics of Plaslok 504, while at the same time, improved impact strength.Data provided by Plaslok Corporation.Plaslok Corporation was purchased by Plastics Engineering Company in March 2000. The Plaslok name is no longer used on any products.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ASTM D792
Apparent Bulk Density 0.550 g/cc
0.0199 lb/in³
ASTM D1895
Water Absorption 0.30 %
0.30 %
ASTM D570
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
Compression; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM D638
Flexural Yield Strength 80.0 MPa
11600 psi
ASTM D790
Flexural Modulus 4.80 GPa
696 ksi
ASTM D790
Compressive Yield Strength 207 MPa
30000 psi
ASTM D695
Izod Impact, Notched 0.270 J/cm
0.506 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 174 °C
345 °F
ASTM D648
UL RTI, Electrical 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical with Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical without Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
Flammability, UL94 V-1

@Thickness 6.35 mm
V-1

@Thickness 0.250 in
V-1

@Thickness 6.35 mm
V-1

@Thickness 0.250 in
Electrical Properties Metric English Comments
Dielectric Strength 8.90 kV/mm
226 kV/in
ASTM D149
Comparative Tracking Index 180 V
180 V
UL 746