Ineos ABS Lustran® ABS E211 LNS013 Pellets (a-methylstyrene-SAN-modified), Extrusion Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer Ineos ABS
Trade Name Lustran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® ABS E211 LNS013 Pellets (a-methylstyrene-SAN-modified), Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® ABS E211 LNS013 is extrusion grade with high heat resistance. It is used for the production of molded plastic articles.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
Test Condition: 60x60x2; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
Test Condition: 60x60x2; ISO 294-4
Melt Flow 6.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 6.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 105 MPa
15200 psi
ISO 2039-1
Tensile Strength, Yield 45.0 MPa
6530 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 15 %
>= 15 %
50 mm/min; acc. ISO 527-1,-2
Elongation at Yield 2.7 %
2.7 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 73.0 MPa
10600 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
15.0 J/cm²

@Temperature 23.0 °C
 71.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2; Parallel to Flow
Deflection Temperature at 0.46 MPa (66 psi) 107 °C
225 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 101 °C
214 °F
ISO 75-1,-2
Vicat Softening Point 108 °C

@Load 5.10 kg
 226 °F

@Load 11.2 lb
 50°C/hour; ISO 306
Flame Spread 55 mm/min

@Thickness 2.00 mm
 2.2 in/min

@Thickness 0.0787 in
 US-FMVSS; ISO 3795
Glow Wire Test 700 °C

@Thickness 2.00 mm
 1290 °F

@Thickness 0.0787 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 IEC 60250
3.1

@Frequency 100 Hz
 3.1

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 35.0 kV/mm

@Thickness 1.00 mm
 889 kV/in

@Thickness 0.0394 in
 IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz
 0.0050

@Frequency 100 Hz
 IEC 60250
0.0090

@Frequency 1.00e+6 Hz
 0.0090

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Solution A, Rating; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
Mold Temperature 70.0 °C
158 °F
Injection Molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
Injection Molding; ISO 294