| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP H 1080 T6 T D Polypropylene, 40% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 40% mineral fillerGood physical and mechanical characteristics, high thermal stability, detergent resistanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ASTM D 955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D 638 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D 638 |
| Elongation at Break | 50 % | 50 % | ASTM D 638 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ASTM D 638 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.150 J/cm @Temperature -20.0 °C |
0.281 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 0.250 J/cm @Temperature 0.000 °C |
0.468 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 0.350 J/cm @Temperature 23.0 °C |
0.656 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 95.0 °C @Load 5.00 kg |
203 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- Nye Lubricants 748A (RL) Synthetic Oil
- Pyrotek C-1 Ceramic fiber paper
- Poco Graphite SUPERSiC® Si-3C Silicon Carbide
- SABIC Innovative Plastics Lexan® BFL2000U PC (Europe-Africa-Middle East)
- Covestro Apec® DP9-9331 High-Heat Polycarbonate, General Purpose (discontinued **)
- PolyOne Edgetek® SF-30CF/000 Polyphenylene Sulfide (PPS), Carbon Fiber Reinforced (discontinued **)
- Saint-Gobain Norton® Fluorglas® Chemfilm® R167 Extruded Expanded PTFE Film (0.010" thick)
- Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Dry)
- Pyrotek TS-81 Thermoset Electrical Insulation Product (Nema Grade: CE)