| Category | Polymer , Thermoplastic , AES Polymer , AES, Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Centrex® 401 AES Extrusion
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Melt Flow | 5.6 g/10 min @Load 10.0 kg, Temperature 230 °C |
5.6 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Tensile Modulus | 1.70 GPa | 247 ksi | ASTM D638 |
| Flexural Yield Strength | 42.1 MPa | 6110 psi | ASTM D790 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm @Temperature -40.0 °C |
1.70 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 5.90 J/cm @Thickness 3.17 mm |
11.1 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Impact Test | 35.0 J @Thickness 3.20 mm |
25.8 ft-lb @Thickness 0.126 in |
Instrumented Impact, Total Energy; 3.2 mm thick, 7.6 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 79.0 µm/m-°C @Temperature 20.0 °C |
43.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C @Thickness 3.17 mm |
174 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C @Thickness 1.60 mm |
122 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 1.60 mm |
122 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 1.60 mm |
122 °F @Thickness 0.0630 in |
UL746B |
| Flammability, UL94 | HB @Thickness 1.43 mm |
HB @Thickness 0.0563 in |
|
| HB @Thickness 1.43 mm |
HB @Thickness 0.0563 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 45 % | 45 % | 60°; Formed; ASTM D523 |
| 75 % | 75 % | 60°; Sheet; ASTM D523 | |
| Transmission, Visible | 0.00 % | 0.00 % | Opaque only |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec @Thickness 3.35 mm |
60 - 120 sec @Thickness 0.132 in |
UL Rating PLC 6 (60-120 sec) |
| Comparative Tracking Index | >= 600 V @Thickness 3.35 mm |
>= 600 V @Thickness 0.132 in |
UL Rating PLC 0 (>600 V) |
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness 3.35 mm |
15 - 30 sec @Thickness 0.132 in |
UL Rating PLC 3 (15-30 sec) |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.43 mm |
>= 120 arcs @Thickness 0.0563 in |
UL Rating PLC 0 (>120 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min @Thickness 1.43 mm |
0.394 - 1.00 in/min @Thickness 0.0563 in |
UL Rating PLC 1 (10-25.4 mm/min.) |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 243 °C | 399 - 469 °F |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® MP 30 Low Density Polyethylene - Injection Molding
- Techmer ES Plaslube® NY-1/SI/2 WT PA66
- Styrolution Terblend® N NM-12 ABS/PA6 (Dry)
- Teknor Apex Sinvicomp SME 6330A Polyvinyl Chloride, Flexible
- Hexcel® HexWeb® HRH-10 - 1/8- 5.0 Aramid Fiber/Phenolic Resin Honeycomb
- Ensinger TECACRYL®
- Chosun Refractories 1400BULK Bulk
- Osprey Metals 440C Stainless Steel Powder (Grade 90% - 22)
Copyright © lookpolymers.com All Rights Reserved