Solvay TECHNYL® A 238 V13 PA66, 13% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 238 V13 PA66, 13% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 13% of glass fiber, heat stabilized, with improved impact resistance, for injection molding.Available in: Europe, Latin America and North AmericaProduct Applications: In addition to primary polyamide properties, TECHNYL ® A 238 V13 offers a very good rigidity/impact resistance compromise, at high temperatures. This grade is used for under bonnet automotive parts, such as: various covers and fasteners. This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0085 cm/cm | 0.0085 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0085 cm/cm | 0.0085 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527 type 1 A |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A |
| Tensile Modulus | 5.50 GPa | 798 ksi | ISO 527 Type 1A |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 3311-xx13D Polyvinyl Chloride, Flexible (PVC, Flexible)
- Stir SpA CT 53 ATC (PVC)
- Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled
- Styron CALIBREâ„¢ 203-22 Polycarbonate Resin
- Unifrax Fiberfrax® Durablanket® HP-S Ceramic Fiber Insulator
- Fainplast Compounds PH 50/AL Flexible PVC, Transparent Extrusion
- Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled
- Sax Polymers SAXATEC 4210 Acrylonitrile Styrene Acrylate
- SABIC Innovative Plastics LNP Thermocomp FF004 PE (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved