PolyOne Edgetek® PI-10CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PI-10CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedElectrically ConductiveInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Water Absorption | 0.21 % @Thickness 3.17 mm |
0.21 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Water Absorption at Saturation | 1.2 % @Thickness 3.17 mm |
1.2 % @Thickness 0.125 in |
Long-Term Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 114 | 114 | ASTM D785 |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.89 GPa | 1000 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10000 ohm | 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FF 20 Low Density Polyethylene - Blown Film Extrusion
- Iran Petrochemical (PCC) Arak EX3 HDPE
- Struktol TPW 101 Processing Additive
- Saint-Gobain Rulon® 142 Grade Bearing/Seal PTFE
- Toho Tenax Besfight® MC Type I (6000 Filament) Nickel Coated Carbon Fiber
- A. Schulman POLYBATCH™ Mahogany 50381 Concentrate Based in Polyethylene
- BASF Elastollan 598 A TPUR
- 3M Scotch® 202 Paper Masking Tape
- Colorite Polymers 6575 General Purpose Vinyl Compound
- Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched
Copyright © lookpolymers.com All Rights Reserved