Idemitsu Kosan Xarec® N WA 7020 SPS, 20% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® N WA 7020 SPS, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystalline Polymer Blend, Glass Filled, Impact Modified. Used in Automotive Electronics applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | |
| Filler Content | 20 % | 20 % | |
| Water Absorption | 0.22 % | 0.22 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | |
| Elongation at Break | 2.9 % | 2.9 % | |
| Tensile Modulus | 7.30 GPa | 1060 ksi | |
| Flexural Yield Strength | 215 MPa | 31200 psi | |
| Flexural Modulus | 6.70 GPa | 972 ksi | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C | 30.0 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 3.10e+15 ohm-cm | 3.10e+15 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D145 |
| Dissipation Factor | 0.034 | 0.034 | IEC 60250 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | 0.00 - 7.0 sec @Thickness 1.50 mm |
0.00 - 7.0 sec @Thickness 0.0591 in |
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | 1 - 3 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | High Ductility | |
| Nylon/SPS blend |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 66 BT N 27 B/IM PA66
- A. Schulman POLYBATCH™ Red 5400 Concentrate Based In Polyethylene
- Ter Hell Plastic Terez® PC 9007 UV Polycarbonate
- A. Schulman POLYBATCH™ FSU-105-E Concentrate Based In LDPE
- Daikin DAI-EL G-551 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 69% Fluorine Content
- Breplast Bretene TS High Density Polyethylene
- 3M FM001 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- Nylene® Naxel™ PC41 Polycarbonate
- SABIC Innovative Plastics Lexan® HPH4504H PPC
Copyright © lookpolymers.com All Rights Reserved