Idemitsu Kosan Xarec® N WA 7010 SPS, 10% Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® N WA 7010 SPS, 10% Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystalline Polymer Blend, Glass Filled. Used in Automotive Electronics applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Filler Content | 10 % | 10 % | Glass |
| Moisture Absorption | 0.450 % | 0.450 % | 24 hours, 50% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm @Thickness 2.00 mm |
0.0055 in/in @Thickness 0.0787 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 4.80 GPa | 696 ksi | ASTM D638 |
| Flexural Strength | 158 MPa | 22900 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 3.70 kJ/m² @Temperature 23.0 °C |
1.76 ft-lb/in² @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 320 °C | 554 - 608 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PP 1396 Conductive Thermoplastic Compound
- Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced
- NOVA Chemicals Sclair® 16A Butene HDPE Film Resin (discontinued **)
- Techmer ES Elastoblend® PA6 IM L W
- Techmer ES HiFill® PA6 GF/B30 HS L BK 30% Glass Fiber/Glass Bead Filled
- Teknor Apex Sinvicomp SIM 6019 Polyvinyl Chloride, Flexible
- A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene
- Hexcel® HexPly® EH04 Epoxy Resin System, IM4 Fiber
- DuPont Performance Polymers Hytrel® HTR8223 BK320 Polyester Elastomer TPC-ET (Unverified Data**)
- DuPont Performance Polymers Delrin® 520MP NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved