Gromax CCP PBT 3040-201 30% Glass Fiber Filled

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Gromax
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Gromax CCP PBT 3040-201 30% Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent mechanic and chemical property Excellent weatherability Excellent wear property Excellent moldability High resistance to fuels, oil, fats and many solventsInformation provided by Gromax Enterprises Corp.
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ASTM D792
Moisture Absorption 0.0400 %

@Time 86400 sec
0.0400 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm

@Thickness 1.60 mm
0.0020 - 0.0040 in/in

@Thickness 0.0630 in
horizontal; ASTM D955
0.0060 - 0.012 cm/cm

@Thickness 1.60 mm
0.0060 - 0.012 in/in

@Thickness 0.0630 in
vertical; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength 132 MPa
19200 psi
ASTM D638
Elongation at Break 3.5 %
3.5 %
ASTM D638
Flexural Strength 195 MPa
28300 psi
ASTM D790
Flexural Modulus 9.81 GPa
1420 ksi
ASTM D790
Izod Impact, Notched >= 0.971 J/cm

@Thickness 6.35 mm
>= 1.82 ft-lb/in

@Thickness 0.250 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 30.0 µm/m-°C
16.7 µin/in-°F
ASTM D696
Melting Point 225 °C
437 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ASTM D648
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ASTM D257
Dielectric Constant 3.7

@Frequency 60.0 Hz
3.7

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 23.0 kV/mm

@Thickness 2.00 mm
584 kV/in

@Thickness 0.0787 in
ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
0.0010

@Frequency 60.0 Hz
ASTM D150
Arc Resistance 100 sec
100 sec
ASTM D495
Processing Properties Metric English Comments
Processing Temperature 240 - 270 °C
464 - 518 °F
Nozzle Temperature 260 - 270 °C
500 - 518 °F
Mold Temperature 40.0 - 120 °C
104 - 248 °F
suitable temperature 60-80°C
Injection Pressure 50.0 - 120 MPa
7250 - 17400 psi
Hold Pressure 30.0 - 80.0 MPa
4350 - 11600 psi
Back Pressure 0.000 - 0.300 MPa
0.000 - 43.5 psi
Screw Speed 60 - 120 rpm
60 - 120 rpm
to be chosen in such a way that plasticizing time is just within cooling time
Descriptive Properties Value Comments
Injection Rate middle-fast