SABIC Innovative Plastics LNP LUBRILOY D20009 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY D20009 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* D20009 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | ASTM D638 |
| Elongation at Break | 84 % | 84 % | ASTM D638 |
| Flexural Strength | 87.0 MPa | 12600 psi | ASTM D790 |
| Flexural Modulus | 2.28 GPa | 331 ksi | ASTM D790 |
| Izod Impact, Notched | 6.99 J/cm | 13.1 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.13 | 0.13 | ASTM D3702 Modified |
| K (wear) Factor | 113 x 10-8 mm³/N-M | 56.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6402 Adhesive
- Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F)
- Techmer ES Plaslube® PC-50/TF/13/SI/2 WT8966 Polycarbonate
- Teknor Apex Telcar® TL-2560F Thermoplastic Elastomer
- Cosmic Plastics K77 Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- Alcoa Toolrite 2011®-T4 Aluminum
- Lubrizol ESTANE® 58201 Ether Based Thermoplastic Polyurethane (European Grade)
- Arkema Group Orgalloy® RS 6635 A Polyamide 6.6 Alloy 35% Glass Fiber reinforced
- BASF Neopolen® P 8225 K 0.03 g/cc Core density; Expanded Polypropylene (Europe)
- BCC Products DP-11-90 Urethane Casting
Copyright © lookpolymers.com All Rights Reserved