Gromax BTG25-FN09N1 Nylon 6 25% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BTG25-FN09N1 Nylon 6 25% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ISO 1183 |
| Moisture Absorption | 0.950 % | 0.950 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Temperature 80.0 °C |
0.0040 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Temperature 80.0 °C |
0.0080 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 71 | 71 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 63.7 MPa | 9250 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 6.5 % | 6.5 % | 50 mm/min; ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 8.70 J/cm² @Temperature 23.0 °C |
41.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1A |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 287 °C | 518 - 549 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2005 XRC Black 20% Filler Content Polypropylene
- SABIC Innovative Plastics Lexan® EX1036T PC (Europe-Africa-Middle East)
- PolyOne Elastamax™ EG-9090 Thermoplastic Elastomer (TPE)
- ExxonMobil Santoprene® 283-40MED Thermoplastic Elastomer (discontinued **)
- Iran Petrochemical (PCC) Arak I3 HDPE
- SABIC Innovative Plastics ULTEM 1010M PEI (Asia Pacific)
- Axiall 3217 Rigid PVC, Extrusion
- Axiall 8903 Moldings & Extrusions Flexible PVC
- Teknor Apex APEX® 3610-90 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved